MECHANIC MCN-DJ002 electrically conductive adhesive 0.2 ml

MECHANIC MCN-DJ002 electrically conductive adhesive 0.2ml after evaporation of the solvent provides 100% electrical conductivity at the connection point. The adhesive has the consistency of a thin paste which, after evaporation of the solvent (thermoplastic resin), dries into a solid form. Full electrical conduction takes place in the solid phase.

parameters:

- conductive agent: powdered silver 80-90%

- silver particle size:

- viscosity (Brookfield RVT, 25C measurement): 13-30Pa.S

- storage temperature: 5-25 ° C

- efficiency: 100-200cm2 / g

- resistance depending on the thickness of the coating: less than 0.5 Ohm / 4-6

- hardness:> = 2H

- long-lasting working temperature: below 70 ° C

- thinner: ethanol (proportions, e.g. 1: 0.7-0.8)

- capacity: 0.2ml

Designed for spot repairs:

- paths and transitions on PCBs

- paths and connections on glass surfaces

- connections on LED panels

- complementing the backlight strip in iPhone 5 / 5S / 6 / 6S / 7 / 7S

(removes static problems (streaks) that appear after the LCD repair process)

Features:

- excellent adhesion to glass and artificial surfaces, ie ABS, PC, PET, PVC, PU

- excellent resistance to moisture

- the possibility of shortening the drying time at higher temperatures

- creates a durable coating on the surface

Recommendations for use:

- coating thickness: 10-20um

- ensure proper ventilation of the room

- keep away from heat / sparking / open fire / hot surfaces

- smoking is forbidden

Drying time:

At room temperature, 2-3 hours depending on the layer thickness and temperature.

After heating the adhesive with hot air (eg a dryer), the pre-drying time is shortened:

- at 60 ° C - 20min

- at 90 ° C - 15min

- at 120 ° C - 5min

- at 135 ° C - 4min

- at 145 ° C - 2min

Complete drying and curing 12-24 hours at room temperature or 145 ° C for 2 minutes